Flow behavior and fracture of Al-Mg-Si alloy at cryogenic temperatures
Danielle Cristina Camilo MAGALH?ES, Andrea Madeira KLIAUGA, Vitor Luiz SORDI

Department of Materials Engineering, Federal University of S?o Carlos-UFSCar, Rod. Washington Luiz, km 235, 13565-905, S?o Carlos–SP, Brazil

Abstract:The tensile and fracture behaviors of AA6061 alloy were investigated in order to provide quantitative data about this alloy at cryogenic temperatures. Specimens of AA6061 alloy were solution heat treated before tensile tests at 298, 173 and 77 K and tested at strain rates in the range from 0.1 to 0.0001 s-1. The results indicate the suppression of the Portevin-Le Chatelier (PLC) effect and dynamic strain aging (DSA) at 77 K. In contrast, at 298 K, a remarkable serrated flow, characteristic of the PLC effect, is observed. Furthermore, the tensile behavior at 77 K, compared with that observed at 173 and 298 K, shows a simultaneous increase in strength, uniform elongation, modulus of toughness, strain-hardening exponent and strain rate sensitivity, which is related to a decrease in the dynamic recovery rate at low temperature. These responses are reflected on the fracture morphology, since the dimple size decreases at 77 K, while the area covered by dimples increases. Comparisons of the Johnson-Cook model show that a good agreement can be obtained for tests at 173 and 77 K, in which DSA is suppressed.

 

Key words: cryogenic temperature; aluminum alloy; flow behavior; strain rate sensitivity; work-hardening behavior; Johnson-Cook model; fracture

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com