Effect of P addition on mineral transition of CaO-Al2O3-SiO2 system during high-temperature sintering
Hai-yan YU, Xiao-lin PAN, Kai-wei DONG, Yan WU

School of Metallurgy, Northeastern University, Shenyang 110819, China

Abstract:The mineral transition, microstructure and self-pulverization as well as the Al2O3 leaching performance of calcium aluminate clinkers with different P additions in CaO-Al2O3-SiO2 system during high-temperature sintering were systematically studied by XRF, XRD, SEM-EDS and DSC-TG technologies. The clinkers sintered at 1350 °C mainly contain 12CaO·7Al2O3, CaO·Al2O3, β-2CaO·SiO2 and γ-2CaO·SiO2. The content of β-2CaO·SiO2 increases while the content of γ-2CaO·SiO2 decreases as the P addition increases. The self-pulverization property of clinkers deteriorates with increasing P addition. P distributes evenly in the clinkers, and inhibits the transformation of β-2CaO·SiO2 to γ-2CaO·SiO2. The cell volumes of 12CaO·7Al2O3 and CaO·Al2O3 decrease and increase respectively as the P addition increases, and P decreases their formation temperatures. The Al2O3 leaching rate of calcium aluminate clinkers decreases obviously with increasing P addition, which decreases form 95.01% to 83.84% as the P addition increases from 0 to 0.85%.

 

Key words: lime-sinter process; calcium aluminate; dicalcium silicate; crystal structure; self-pulverization performance; leaching

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com