交流阻抗谱在炉渣电导率测定中的应用
鲁雄刚1, 2, 李福shen1, 李丽芬1, 周国治1

(1. 北京科技大学固体电解质冶金测试技术国家专业实验室, 北京100083;
2. 上海大学材料科学与工程学院,上海200072
)

摘 要: 利用电化学交流阻抗谱法对CaO-SiO2-Al2O3-FeOx渣系的电导进行了研究。结果表明,随着渣相中氧化亚铁浓度的增大, 温度系数逐渐减小; 三价铁离子对电导率的影响随渣相中铁氧化物浓度的增大而显著, 但当铁氧化物浓度小于20%(摩尔分数)时, 三价铁离子对电导率的影响较小;CaO-SiO2-Al2O3 - Fe2O3渣系中存在电子导电,电子电导率约为10-3~10-2S·cm-1

 

关键字:  炉渣; 电导率; 阻抗谱

Application of AC impedance for measuring resistance of slag
LU Xiong-gang1, 2, LI Fu-shen1, LI Li-fen1, ZHOU Guo-zhi(Kouchih Chou)1

1. Laboratory on Solid Electrolytes and Metallurgical Testing Techniques, University of Science and Technology Beijing, Beijing 100083, P.R.China;
2. School of Materials Science and Engineering, Shanghai University, Shanghai 200072, P.R.China

Abstract:The electrochemical AC impedance for measuring the resistance of CaO-SiO2-Al2O3-FeOx slag system was worked out. The experimental results suggest that the temperature coefficient decreases as the content of iron oxide in slag increases. The effect of ferric ion on electrical conductivity is more pronounced at high iron oxide concentrations, but when the mole fraction of iron oxide is below 20%, the effect of ferric ions can be neglected. The experimental data show also that electronic conductance exists in CaO-SiO2-Al2O3 - Fe2O3 slag system. It can be estimated that electronic conductance is in the range of 10-3S·cm-1 to 10-2 S·cm-1.

 

Key words: slags; conductivity; complex impedance

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com