In-situ crack propagation observation in fully lamellar Ti-49%Al alloy①
LU Yong-hao(陆永浩)1,2, ZHANG Yong-gang(张永刚)1, QIAO Li-jie(乔利杰)1,
WANG Yan-bin(王燕斌)1, CHEN Chang-qi(陈昌鹿其)1, CHU Wu-yang(褚武扬)1

1. Department of Materials Physics, University of Science and Technology Beijing,
Beijing 100083, P.R.China;
2. Department of Materials Science and Engineering,
Beijing University of Aeronautics and Astronautics, Beijing 100083, P.R.China

Abstract:The fracture mechanism of lamellar Ti-49%Al alloy was investigated through studying the interactions between crack and lamellae or grain boundary. The results indicated that the nucleation and propagation mechanisms of crack depends on not only the lamellar orientations within grain but also the types of grain boundaries. When the angle between tensile axis and lamellae is relatively large, the main crack parallel to the lamellae propagates by nucleation, growth and linkage with interfacial microcracks. When the tensile axis is nearly parallel to the lamellae, the main crack perpendicular to the lamellae propagates by nucleation, growth and linkage with two types of microcracks, e.g. translamellar microcrack and interface delamination. In addition, the interlock grain boundary nearly parallel to the tensile axis is benefit to fracture toughness, the grain boundary nearly perpendicular to the tensile axis is bad for the toughness.

 

Key words: TiAl alloy; lamellae; crack; grain boundary; fracture mechanism

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com