Cold extrusion deformation behavior of medium carbon steel after quenching and tempering
HU Cheng-liang(胡成亮)1, ZHAO Zhen(赵 震)1, YIN Guan-ren(尹冠人)1,
YUAN Zhao-feng(袁兆峰)2, XU Xiang-long(徐祥龙)2

1. Department of Plasticity Technology, Shanghai Jiao Tong University, Shanghai 200030, China;
2. Jiangsu Sunway Precision Forging Co., Ltd., Dafeng 224100, China

Abstract:By taking 40Cr as a specific object, cold extrusion deformation behavior of medium carbon steel after quenching and tempering was studied by experimental works. The influence of deformation extent (10%−50%), cone angle of die (90˚−120˚), hardness after quenching and tempering (HRC21−29) and lubricated condition on the forming load was analyzed. The results show that there is no central bursting and micro crack in the inner of the extruded specimen, and the forming quality is good. The double-peak phenomenon takes place at the front-end of the specimen; the double-peak index increases with deformation extent, and larger deformation can avoid the double-peak phenomenon. The deformation extent is the most important influencing factor, and the lubricated condition almost has no influence, which means that the phosphate coating plus soap process is still a proper lubrication method for cold extrusion of medium carbon steel after quenching and tempering. By investigating the microscopic structure before and after deformation, the initial equiaxed grain is elongated in the extrusion direction, and this feature is more significant at the front-end of specimen.

 

Key words: medium carbon steel; quenching and tempering; cold extrusion; deformation behavior; microstructure

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com