中国有色金属学报(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 16 No. 3 June 2006 |
（1. Key Laboratory of Structure and Heredity of Materials, Ministry of Education, Shandong University,Ji’nan 250061, China;
2. Quality and Technology Supervision Bureau, Weifang 261031, China）
Abstract:Ribbons of amorphous Cu-Ti-Ni alloys were prepared by the melt spinning method. The amorphous structure of these ribbons was confirmed by X-ray diffractametry and transmission electron microscopy. The effect of Ni on the glass-forming ability of Cu-Ti-based alloys was studied by differential scanning calorimetry(DSC). It is found that the supercooled liquid region, ΔTx value shows the maximum value of 61℃ at x=10 in the Cu50Ti50−xNix (x=0, 5, 10, 15 mole fraction, %) system. And the reduced glass transition temperature, Trg, is smaller than 0.45. The glass forming ability(GFA) of Cu-Ti alloy is not effectively promoted by Ni addition.
Key words: Cu-Ti-based alloys; glass-forming ability; melt-spinning method; deep eutectics