Preparation and properties of porous ceramics from spodumene flotation tailings by low-temperature sintering
Jie YANG1, Long-hua XU1,2, Hou-qin WU1,3, Jiao JIN4

1. Key Laboratory of Solid Waste Treatment and Resource Recycle (Ministry of Education), Southwest University of Science and Technology, Mianyang 621010, China;
2. State Key Laboratory for Environment-friendly Energy Materials, Southwest University of Science and Technology, Mianyang 621010, China;
3. School of Civil Engineering and Architecture, Southwest University of Science and Technology, Mianyang 621010, China;
4. School of Traffic and Transportation Engineering, Changsha University of Science and Technology, Changsha 410114, China

Abstract:Porous ceramics were prepared with spodumene flotation talings (SFT), kaolin and low-melting point glass (LPG) powder, whose pores were formed by the chemical reaction of hydrogen peroxide (H2O2). LPG was used to reduce the sintering temperature of porous ceramics and kaolin was used to realize the adsorption to methylene blue (MB) of porous ceramics. The average flexural strength, compressive strength, apparent porosity, water absorption and maximum MB adsorption capacity were 5.60 MPa, 4.66 MPa, 52.27%, 44.32% and 0.7 mg/g, respectively. Moreover, the results of orthogonal experiments present that the sintering temperature and the dosage of H2O2 had great influence on the mechanical properties and apparent porosity of porous ceramics, respectively. The main reason for the improvement of mechanical properties of porous ceramics was that LPG gradually became soft with increasing the sintering temperature, which made the mineral particles adhere to each other closely. Kaolinite was not completely converted into metakaolin at 550 °C, which might be the main reason why porous ceramics had adsorption properties.

 

Key words: spodumene flotation tailings; porous ceramics; low-temperature sintering; absorption

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com