中国有色金属学报(英文版)
Transactions of Nonferrous Metals Society of China
Vol. 31 No. 7 July 2021 |
(School of Materials Science and Engineering, Northwestern Polytechnical University, Xi’an 710072, China)
Abstract:For precise plastic deformation, microstructure control is essential especially for β-solidifying γ-TiAl alloy with duplex structure. Based on stereology, the microstructure of isothermally compressed γ-TiAl alloy was divided into β0 grains, remnant α2/γ lamellar colonies, α2 and γ grains. The results show that the volume fraction of β0 grains slightly increases in the isothermally compressed γ-TiAl alloy with the increase of height reduction. Meanwhile, the volume fractions of remnant α2/γ lamellar colonies and α2 grains decrease. However, the volume fraction of γ grains increases from 64.39% to 78.47%. According to the quantitative results, the α→γ phase transformation was investigated in-depth, and it is found that isothermal compression accelerates the α→γ phase transformation. The first α→γ phase transformation is similar to ledge-controlled transformation, through which remnant α2/γ lamellar colonies finally convert into γ grains in isothermal compression. The second is achieved by α/γ phase interface immigration.
Key words: TiAl alloy; stereology; digital image analysis; microstructure; phase transformation