In-situ investigation of deformation behavior and fracture forms of Ti/Al/Mg/Al/Ti laminates
Hui-hui NIE1,2, Liu-wei ZHENG3, Xiao-ping KANG4, Xin-wei HAO2,5, Xian-rong LI2,5, Wei LIANG2,3,5

1. College of Mechanical and Vehicle Engineering, Taiyuan University of Technology, Taiyuan 030024, China;
2. Shanxi Key Laboratory of Advanced Magnesium-based Materials, Taiyuan University of Technology, Taiyuan 030024, China;
3. Instrumental Analysis Center, Taiyuan University of Technology, Taiyuan 030024, China;
4. Shanxi Institute of Energy, Taiyuan 030006, China;
5. College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, China

Abstract:In-situ bending and stretching were conducted on hot-rolled and annealed Ti/Al/Mg/Al/Ti laminates, with a focus on crack initiation and propagation of intermetallics and component layers, which helps to clarify their deformation behavior and fracture forms. The results show that delamination is the early fracture form of laminate with or without intermetallics at Al/Mg interface, so Al/Mg interfacial bonding strength determines the mechanical properties of laminate. Various and irregular intermetallics cracks lead to Al/Mg interface delamination in annealed laminate and help to release stress. Necking and fracture of component layers are observed at the late deformation stage, and the sequence is Al, Mg and Ti layers, resulting from their strength. Angle between crack propagation direction and stretching direction of Mg layer both in rolled and annealed laminates is around 45° due to the effect of shear deformation, and crack convergence leads to final complete fracture of Mg layer.

 

Key words: Ti/Al/Mg/Al/Ti laminate; in-situ test; intermetallics; crack initiation; fracture form

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com