Effect of salt-assisted reduction method on morphologies and size of metallic tungsten particles
Ze-peng Lü1,2, Kai-liang JIAN1,2, Jie DANG1,2

1. College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China;
2. Chongqing Key Laboratory of Vanadium-Titanium Metallurgy and Advanced Materials, Chongqing University, Chongqing 400044, China

Abstract:A simple method was proposed to produce tungsten (W) particles with controllable shape and size by employing the salt-assisted hydrogen reduction. W particles with controlled shape and size were prepared by adjusting the amount of chlorine salts and the temperature. After adding salt additives, the dispersibility of final particles was obviously improved and more adequate growth of particles was obtained. It was found that the effect of NaCl and LiCl is particularly significant. The average sizes of the obtained W particles at 1038 K after adding 0.1 wt.% NaCl and 0.1 wt.% LiCl were 0.924 and 1.128 μm, respectively. With the increase of temperature and amount of chlorine salts, the dispersity of the produced W particles became much better, the size of W sub-particles was increased, and the shape of W sub-particles was changed from spherical to polyhedral. At 1349 K, the addition of chlorine salts even multiplied the particle size, and the average sizes of W particles with 1 wt.% NaCl and 1 wt.% LiCl were raised up to 21.367 and 29.665 μm, respectively. Based on the conventional pseudomorphic transformation and chemical vapor transport mechanisms, the effects of adding salts on the reaction mechanism were investigated in detail as well.

 

Key words: tungsten particles; salt-assisted hydrogen reduction; chlorine salt; morphology; size; controllable synthesis

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com