Viscoplastic friction and microstructural evolution behavior of laser-clad Co-Cr-Ni-Mo coating
Rui-di LI1,2, Jing-long LI1,2, Yi LIANG1,2, Cheng-zhong JI1,2, Tie-chui YUAN3

1. State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, China;
2. Shaanxi Key Laboratory of Friction Welding Technologies,Northwestern Polytechnical University, Xi’an 710072, China;
3.State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China

Abstract:The viscoplastic friction and nanostructure formation mechanism of laser-clad Co-based coating were studied by rotary friction between laser-clad Co-Cr-Ni-Mo coating and WC-Co rod. The friction coefficient, friction interface temperature and axial displacement—time curves during rotary friction process were measured. The results showed that all the curves firstly experienced rising stage and then steady stage. The rising stage corresponded to sliding friction while the steady stage corresponded to viscoplastic friction. After viscoplastic friction processing, three typical zones of viscoplastic deformation zone, thermo-mechanically affected zone, and original laser-clad zone can be observed successively from the friction surface to the interior. The viscoplastic deformation significantly crushed the network M23C7 phase in original laser-clad zone and made it dispersively distributed with equiaxial shape and in nano-scale. The viscoplastic zone, in width of 37-131 μm, is mainly characterized by refined M23C7 and α-Co phase with grain size bellow 50 nm, and even a small quantity of amorphous. Thus, the hardness of viscoplastic zone about HV997 was improved compared with the hardness of original laser-clad zone about HV600.

 

Key words: viscoplastic deformation; severe plastic deformation; laser cladding; Co-Cr-Ni-Mo coating; nanostructure; rotary friction

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com