Yield strength prediction of rolled Al-(1.44-12.40)Si-0.7Mg alloy sheets under T4 condition
Guang-dong WANG1, Ni TIAN1,2, Jing-yi CAO1, Yi-ran ZHOU1, Gang ZHAO1,2, Liang ZUO1,2

1. School of Materials Science and Engineering, Northeastern University, Shenyang 110819, China;
2. Key Laboratory for Anisotropy and Texture of Materials, Ministry of Education, Northeastern University, Shenyang 110819, China

Abstract:The effects of Si content on the microstructure and yield strength of Al-(1.44-12.40)Si-0.7Mg (wt.%) alloy sheets under the T4 condition were systematically studied via laser scanning confocal microscopy (LSCM), DSC, TEM and tensile tests. The results show that the recrystallization grain of the alloy sheets becomes more refined with an increase in Si content. When the Si content increases from 1.44 to 12.4 wt.%, the grain size of the alloy sheets decreases from approximately 47 to 10 μm. Further, with an increase in Si content, the volume fraction of the GP zones in the matrix increases slightly. Based on the existing model, a yield strength model for alloy sheets was proposed. The predicted results are in good agreement with the actual experimental results and reveal the strengthening mechanisms of the Al-(1.44-12.40)Si-0.7Mg alloy sheets under the T4 condition and how they are influenced by the Si content.

 

Key words: wrought Al-(1.44-12.40)Si-0.7Mg alloy sheets; T4 condition; Si content; yield strength prediction; strengthening mechanism

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com