Effect of prestressed ultrasonic peen forming parameters on bending curvature and spherical deformation of plate
Tao ZHANG1,2, Lei LI1, Shi-hong LU1, Jia-bin ZHANG1, Zhen ZHOU1, Hai GONG2

1. College of Mechanical and Electrical Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China;
2. State Key Laboratory for High Performance Complex Manufacturing, Central South University, Changsha 410083, China

Abstract:The elastic prestressed ultrasonic peen forming (UPF) was adopted in order to solve problems of insufficient bending deformation and large spherical deformation of plate during free UPF. The theoretical analysis of prestressed UPF and the influence of elastic prebending moment on deformation were analyzed. Spherical deformation coefficient was defined to quantificationally describe the spherical deformation. Experiments were conducted to compare the differences between free UPF and prestressed UPF processes and the effects of processing parameters on bending curvature and spherical deformation coefficient were studied. The results show that peening trajectory in chordwise direction is beneficial to enlarging spanwise bending deformation and decreasing spherical deformation coefficient. Large prebending curvature is helpful to increase spanwise bending deformation and decrease chordwise deformation, thereby obviously decreasing spherical deformation coefficient. Large spanwise deformation can be obtained under large firing pin velocity, small plate thickness and small offset distance. Large firing pin velocity plays a positive role in decreasing spherical deformation, while plate thickness and offset distance have little effect on it. Above all, prebending curvature and peening trajectory are the most important factors during prestressed UPF process. This study provides guidance for parameters optimization of prestressed UPF for wing plate with large thickness.

 

Key words: prestressed ultrasonic peen forming; forming curvature radius; spherical deformation coefficient

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com