Abstract:To prepare the three-dimensional braided carbon fiber reinforced mullite (3D C/mullite) composites, an Al₂O₃-SiO₂ sol with a solid content of 20% (mass fraction) and an Al₂O₃/SiO₂ mass ratio of 2:1 was selected as the raw material. Characteristics and mullitization of the sol were analyzed throughly. It is found that the formation of mullite is basically completed at 1300 °C and the gel powders exhibit favorable sintering shrinkage. The 3D C/mullite composites without interfacial coating were fabricated through the route of vacuum impregnation-drying-heat treatment. Satisfied mechanical properties with a flexural strength of 241.2 MPa and a fracture toughness of 10.9 MPa？m^1/2 are obtained although the total porosity reaches 26.0%. Oxidation resistances of the composites at 1200, 1400 and 1600 °C were investigated. Due to the further densification of matrix, the 3D C/mullite composites show tiny mass loss and their mechanical properties are well retained after oxidation at 1600 °C for 30 min.

Key words: carbon fiber reinforced mullite composites; Al₂O₃-SiO₂ sol; mechanical properties; oxidation resistance