低于β相相变温度时TC4钛合金搅拌摩擦焊接头的成形及拉伸性能
王 月1,姬书得1,李政玮1,柴 鹏2

(1. 沈阳航空航天大学 航空航天工程学部,沈阳 110136; 2. 北京航空航天大学 机械工程与自动化学院,北京 100191)

摘 要: 利用轴肩直径为15 mm的钨铼合金搅拌头对2.5 mm厚TC4钛合金进行搅拌摩擦焊,重点分析接头成形、显微组织与拉伸性能。结果表明:焊核区的横截面形貌呈现典型的“碗形”;当转速小于200 r/min时,焊接过程中的温度峰值低于β相相变温度。组成焊核的搅拌针作用区常出现“撕裂”型缺陷,其主要与焊接过程中的焊接拉应力有关;降低搅拌头的旋转速度有利于减小、甚至消除“撕裂”型缺陷。低于相变温度下获得的无缺陷焊接接头的抗拉强度几乎与母材的等同,拉伸测试后的断口由大量韧窝组成,为典型的韧性断裂。

 

关键字: TC4钛合金;搅拌摩擦焊;抗拉强度;撕裂型缺陷;相变温度

Formation and tensile properties of friction stir welded TC4 titanium alloy joint below β-phase transus temperature
WANG Yue1, JI Shu-de1, LI Zheng-wei1, CHAI Peng2

1. Faculty of Aerospace Engineering, Shenyang Aerospace University, Shenyang 110136, China; 2. School of Mechanical Engineering and Automation, Beihang University, Beijing 100191, China

Abstract:TC4 titanium alloy with thickness of 2.5 mm was friction stir welded using W-Re rotational tool with shoulder diameter of 15 mm. The formation, microstructure and tensile property of FSW joint were mainly discussed. The results show that nugget zone (NZ) of cross section presents typical bowl-like shape. When rotating speed is lower than 200 r/min, the peak temperature during welding is below β-phase transus temperature. The tearing defect often appears in pin affected zone of NZ, which results from the welding tensile stress during welding. Decreasing the rotating speed is beneficial to reduce and even eliminate the tearing defect. The defect-free FSW joint attained below β-phase transus temperature owns high tensile strength, which is almost equal to that of base metal. The fracture surface is composed of plenty dimples, presenting the typical ductile fracture.

 

Key words: TC4 titanium alloy; friction stir welding; tensile strength; tearing defect; phase transus temperature

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com