过共晶Al-Si合金P吸收率的影响因素
胡恺琪1,蒋 伟1,朱向镇1,张 茜1,孙谦谦2,刘相法1

(1. 山东大学 材料液固结构演变与加工教育部重点实验室,济南 250061; 2. 山东大学 山东吕美熔体技术有限公司,济南 250061)

摘 要: 采用含P中间合金细化过共晶铝硅合金时,P吸收率是影响合金最终P残留量和Si细化效果的关键因素。研究P吸收率与中间合金种类、熔炼工艺参数以及耦合添加外来微米粒子的相关性,并分析其与AlP相在熔体中演变行为的内在联系。结果表明:熔炼工艺相同时,5种中间合金的吸收率有一定差异,杆状Al-3P的P吸收率最高,可达80%;而Cu-14P的最低,仅为13%。随着熔体温度升高,P吸收率显著提高;随着保温时间延长,P吸收率呈现先增加后减小的趋势;保温90 min时,P吸收率达到极大值;随着加入量增加,P吸收率呈现不断下降趋势。此外,在铝合金熔体中引入与AlP有结构匹配关系的TiB2、TiC等微米粒子,可与未溶解之AlP耦合在一起,起到固定AlP粒子的作用,显著提高P吸收率。

 

关键字: Al-Si合金;初晶Si;P吸收率;工艺参数;晶粒细化

Affecting factors of P absorption rate of hypereutectic Al-Si alloys
HU Kai-qi1, JIANG Wei1, ZHU Xiang-zhen1, ZHANG Qian1, SUN Qian-qian2, LIU Xiang-fa1

1. Key Laboratory of Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan 250061, China; 2. Shandong Al and Mg Melt Technology Company Limited, Shandong University, Jinan 250061, China

Abstract:The phosphorous absorption rate is an important parameter for the refining process of hypereutectic Al-Si alloys, which not only influences final P content, but also reflects the evolution of AlP phase in the melt. The changing rules of P absorption rate were studied as kinds of master alloys, the processing parameters, coupling relationship of added solid particles varied. The experimental results show that Al-3P rod alloy appears the highest absorption rate (80%), while Cu-14P appears the lowest absorption rate (13%) under the same melting condition. The higher holding temperature contributes to superior P absorption rate while the more addition results in the lower. As holding time extends, P absorption rate first increases then decreases when achieving the maximum level at 90 min. Moreover, adding proper solid particles, such as TiB2 and TiC, which have a good structural matching relationship with AlP crystal, can dramatically increase P absorption rate.

 

Key words: Al-Si alloys; primary silicon; P absorption rate; processing parameters; grain refinement

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com