Microstructure characterization of Al-cladded Al-Zn-Mg-Cu sheet in different hot deformation conditions
Bin LIAO1, Xiao-dong WU1, Chang-jian YAN1, Zheng LIU1, Yan-li JI2, Ling-fei CAO1, Guang-jie HUANG1, Qing LIU1

1. College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China; 2. Suzhou Branch, Chinalco Materials Application Research Institute Co., Ltd., Suzhou 215026, China

Abstract:Al-cladded Al-Zn-Mg-Cu sheets were compressed up to 70% reduction on a Gleeble-3500 thermo-mechanical simulator with temperatures ranging from 380 to 450 °C at strain rates between 0.1 and 30 s-1。The microstructures of the Al cladding and the Al-Zn-Mg-Cu matrix were characterized by electron back-scattered diffraction (EBSD) and X-ray diffraction (XRD). The microstructure is closely related to the level of recovery and recrystallization, which can be influenced by deformation temperature, deformation pass and deformation rate. The level of recovery and recrystallization are different in the Al cladding and the Al-Zn-Mg-Cu matrix. Higher deformation temperature results in higher degree of recrystallization and coarser grain size. Static recrystallization and recovery can happen during the interval of deformation passes. Higher strain rate leads to finer sub-grains at strain rate below 10 s-1; however, dynamic recovery and recrystallization are limited at strain rate of 30 s-1 due to shorter duration at elevated temperatures.


Key words: Al-Zn-Mg-Cu alloy; Al cladding; hot compression; recovery; recrystallization

ISSN 1004-0609
CN 43-1238/TG

ISSN 1003-6326
CN 43-1239/TG

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱