磁控溅射制备CrMoAlN梯度薄膜的抗高温氧化性能
王宇星,楼白杨,潘 健,张 侠

(浙江工业大学 材料科学与工程学院,杭州 310032)

摘 要: 采用非平衡磁控溅射离子镀技术在M2工具钢和单晶Si表面沉积CrMoAlN梯度薄膜,并在静态空气中进行600、700、800、900 ℃的高温氧化实验。采用XRD、SEM、XPS、纳米压痕和划痕实验等研究,结果表明:CrMoAlN薄膜呈现与CrN相似的面心立方结构,主要以CrN、AlN和γ-Mo2N形态存在。经800 ℃氧化2 h后,CrMoAlN薄膜基本保持常温时的晶体结构与力学性能。随着氧化温度继续升高,薄膜表层的MoO3加速挥发,破坏由Cr2O3和Al2O3组成的致密氧化层,薄膜表面出现细小孔隙,薄膜氧化程度加剧。经900 ℃氧化2 h后,CrMoAlN薄膜的力学性能和膜/基结合强度均出现明显下降。

 

关键字: CrMoAlN梯度薄膜;磁控溅射;微观结构;高温氧化

High temperature oxidation resistance of CrMoAlN gradient coatings prepared by unbalanced magnetron sputtering
WANG Yu-xing, LOU Bai-yang, PAN Jian, ZHANG Xia

Faculty of Materials Science and Engineering, Zhejiang University of Technology, Hangzhou 310032, China

Abstract:CrMoAlN gradient coatings were deposited on M2 and silicon wafers by closed-field unbalanced magnetron sputtering ion plating(CFUMSIP)technique, and their high-temperature oxidation behaviours were studied after static oxidation tests in air at different temperatures (600, 700, 800, 900 ℃) for 2h. The chemical composition, structural, hardness and adhesive/cohesive strength of the coatings were characterized by EDS, XRD, XPS, SEM, nanoindentation and scratch test. The experimental results show that CrMoAlN coatings exhibit a single phase cubic structure. After oxidation at 800 ℃ for 2 h, the CrMoAlN coatings still retain basically their crystalline structure and mechanical properties. The volatilization reaction rate of MoO3 increases, the dense and protective oxide layer consisting of Cr2O3 and Al2O3 is broken. The porous become clearly observable on the surface of the coating, which provides fast diffusion paths for oxygen and cations, and thus promotes the growth rates of oxide scales. After oxidation at 900 ℃ for 2 h, the mechanical properties and adhesive strength decrease drastically.

 

Key words: CrMoAlN gradient coating; magnetron sputtering; microstructure; high temperature oxidation

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com