Dependence of microstructural, mechanical and electrical properties on growth rates in directional solidified Zn-Al-Bi eutectic alloy
Yasin KARAMAZI1, ümit BAYRAM2, P?nar ATA3, Sezen AKS?Z4, Kaz?m KE?L?O?LU2, Necmettin MARA?LI5

1. Department of Physics, Institute of Science and Technology, Erciyes University, Kayseri 38039, Turkey;
2. Department of Physics, Faculty of Science, Erciyes University, Kayseri 38039, Turkey;
3. Department of Physics, Institute of Science and Technology,
Nev?ehir Hac? Bekta? Veli University, Nev?ehir 50300, Turkey;
4. Department of Physics, Faculty of Arts and Sciences, Nev?ehir Hac? Bekta? Veli University, Nev?ehir 50300, Turkey;
5. Department of Metallurgical and Materials Engineering, Faculty of Chemistry and Metallurgical Engineering,
Y?ld?z Technical University, Davutpa?a-Esenler, ?stanbul 34220, Turkey

Abstract:Zn-5%Al-0.2%Bi (mass fraction) alloy was directionally solidified upward at a constant temperature gradient with a wide range of growth rates using a Bridgman-type directional solidification furnace. The eutectic spacings, microhardness, ultimate tensile strength and electrical resistivity for directionally solidified Zn-Al-Bi alloy were measured. Dependence of eutectic spacings, microhardness, ultimate tensile strength and electrical resistivity on growth rates was obtained by linear regression analysis. The results obtained in the present work for low growth rates (smaller than 450.0 μm/s) are in good agreement with experimental results obtained in previous work for directional solidified Zn-Al eutectic alloy with a similar growth rate but differs from the Jackson-Hunt eutectic theory and those obtained in previous experimental works at higher growth rates. The critical growth rate might be 450.0 μm/s for the Zn-Al-Bi eutectic alloy. From the plot of heat flow versus temperature, enthalpy of fusion, specific heat difference between liquid and solid phases and melting temperature for the Zn-Al-Bi alloy are found to be 112.55 J/g, 0.291 J/(g?K) and 660.20 K, respectively.

 

Key words: directional solidification; zinc-aluminum alloy; microstructure; microhardness; tensile strength; electrical properties

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com