Abstract:The internal friction behavior of Al green power compact duxing the sintering process was studied as a function of temperature. The internal friction measurements were performed from room temperature to 600 °C. Two typical internal friction peaks were detected corresponding to heating and cooling processes, respectively. The heating peak corresponds to a recrystallization process of deformed Al particles, which is influenced by many extrinsic parameters, such as measuring frequency, strain amplitude, heating rate, power particle size and compacting pressure. However, the intrinsic nature of the peak is originated from the micro-sliding of the weak-bonding interfaces between Al particles and increased dislocation density induced in compressing. The cooling peak with the activation energy of (1.64±0.06) eV is associated with the grain boundary relaxation, which can be interpreted as the viscous sliding of grain boundaries. The similar phenomena are also found in the Mg green powder compact.

Key words: Al powder compact; internal friction; sintering; grain boundary