中国有色金属学报(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 25 No. 12 December 2015 |
（1. College of Materials Engineering, Panzhihua University, Panzhihua 617000, China;
2. College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China）
Abstract:A systematic investigation on the effect of milling time on carbothermic reduction of ilmenite was carried out by a combination of thermal analysis, X-ray diffraction (XRD), scanning electron microscopy (SEM) and particle size analysis. It was shown that the graphite crystalline structure was easily destroyedalong the (002) crystal plane during milling process. The particle size of ilmenite/graphite mixture was largely decreased and a fully mixed composite structure was obtained after milling for 4 h at high milling intensity. Milling exerts positive effect on the decreasing temperatures of ilmenite reduction andgradual deoxidizing of titanium oxides was completed.
Key words: milling time; carbothermic reduction; ilmenite