中国有色金属学报(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 25 No. 10 October 2015 |
（1. Department of Mining, Petroleum and Metallurgical Engineering, Faculty of Engineering,
Cairo University, Giza 12613, Egypt;
2. Central Metallurgical Research & Development Institute, P.O. Box 87, Cairo, Egypt;
3. Toyota Technological Institute, 2-12-1 Hisakata, Tempaku, Nagoya 468-8511, Japan）
Abstract:Billets of A356 aluminum alloy were treated using ultrasonic vibrations during solidification. The billets were reheated to the semisolid state at different routes to optimize the procedure. Billets were, then, thixocast using a die casting machine. The results showed that the ultrasonic-treated billets exhibited finely distributed α(Al) globules after reheating and thixocasting. The thixocast ultrasonic-treated billets showed higher ultimate tensile strength and elongation compared with the untreated billets. Moreover, the thixocast parts showed a tendency to ductile fracture under tension when made from ultrasonic-treated billets, while those made of untreated billets showed brittle fracture with obvious straight facets. These results revealed the feasibility and competence of ultrasonic melt treatment as a potential route for preparing billets for thixocasting.
Key words: A356 alloy; semi-solid forming; ultrasonic treatment; reheating; thixocasting; tensile property