热挤压AZ31镁合金单向压缩变形的应变硬化行为
周德智,鲁 月,马 茹,王轶农

(大连理工大学 材料科学与工程学院,大连 116024)

摘 要: 对AZ31镁合金热挤压棒材在室温下沿挤压方向分别进行了应变为3%、6%、10%的单向压缩实验。利用OM、XRD和EBSD等技术研究了不同压缩应变量下的显微组织、织构及应变硬化的演变特征。结果表明:具有{0002}纤维织构的热挤压态AZ31镁合金沿着挤出方向压缩时,产生显著的应变硬化效应。其塑性变形可大致分为3个阶段:初始阶段主要发生{101()2}拉伸孪生,表现为较低的应变硬化速率和应变硬化速率的急剧减小;随着压缩应变量的增加,孪晶界逐渐扩展,直至部分晶粒发生完全孪生,基面织构强度逐渐增强;拉伸孪晶生长所造成的强{0002}基面织构是产生高应变硬化速率的主要原因;应变硬化速率第Ⅱ~Ⅲ阶段的转折点大致与拉伸孪晶的生长停滞相对应。

 

关键字: AZ31镁合金;拉伸孪生;滑移;压缩变形;孪晶界

Strain hardening behavior during uniaxial compression of as-extruded AZ31 magnesium alloy
ZHOU De-zhi, LU Yue, MA Ru, WANG Yi-nong

School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, China

Abstract:Uniaxial compression tests were carried out on an as-extruded AZ31 magnesium alloy along extrusion direction at the strain of 3%, 6% and 10%, respectively, at room temperature. The evolution of microstructures, textures and strain hardening behavior were examined by OM, XRD and EBSD. The results show that the present as-extruded magnesium alloy with {0002} fiber texture exhibits distinct three plastic deformation stages. {101()2} tension twinning takes place at the first stage of the plastic deformation, which results in the low strain hardening rate and rapid decrease in strain hardening rate. With increasing the compressive strain, {101()2} twin boundaries gradually extend until some grains are entirely consumed by the twinning extension, which results in the strong basal texture. The increasing high strain hardening rate are mainly attributed to the formation of strong basal texture. The deformation transition from stage Ⅱ to stage Ⅲ roughly corresponds to the stop of {101()2} twin extending.

 

Key words: AZ31 magnesium alloy; tension twining; slip; compressing deformation; twinning grain boundary

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com