Influence of I-phase and W-phase on microstructure and mechanical properties of Mg-8Li-3Zn alloy
Guo-bing WEI1, Xiao-dong PENG1,2, Bao ZHANG1, Amir HADADZADEH3, Tian-cai XU1, Wei-dong XIE1,2

1. College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China;
2. National Engineering Research Center for Magnesium Alloys, Chongqing University, Chongqing 400044, China;
3. Department of Mechanical and Mechatronics Engineering, University of Waterloo, Waterloo ON N2L 3G1, Canada

Abstract:Microstructures and mechanical properties of LZ83-xY alloys containing I-phase and W-phase were investigated by XRD, OM, SEM and EDS. The experimental results show that the content of I-phase and W-phase changes by varying Zn/Y mass ratio in the LZ83-xY alloys. The cohesion of I-phase/α-Mg eutectic pockets can enhance the strength in the as-cast LZ83-0.5Y and LZ83-1.0Y alloys, while the W-phase has no obvious strengthening effect on the LZ83-1.5Y alloy. In the extruded alloys, the I-phase and W-phase were extruded into the particles with nanoscale size in the β-Li matrix phase. The dispersion strengthening of W-phase was more obvious because of the higher volume fraction. The ultimate tensile strength of extruded LZ83-1.5Y alloy is up to 238 MPa while the elongation is up to 20%.

 

Key words: Mg-8Li-3Zn alloy; I-phase; W-phase; mechanical properties; as-cast microstructure

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com