Pd添加对Zr-4合金在LiOH水溶液中耐腐蚀性能的影响
张金龙1,2,梁 楠1,2,赵寒沛1,2,苟少秋1,2,姚美意1,2,周邦新1,2

(1. 上海大学 微结构重点实验室,上海 200444;
2. 上海大学 材料研究所,上海 200072
)

摘 要: 采用静态高压釜腐蚀实验研究添加微量Pd元素的Zr-4合金在(360 ℃,18.6 MPa)条件下0.01 mol/L LiOH水溶液中的耐腐蚀性能,采用TEM和SEM研究合金和氧化膜的显微组织。结果表明:添加0.05%~0.2% Pd(质量分数)均可明显改善Zr-4合金在LiOH水溶液中的耐腐蚀性能,其中添加0.1% Pd时改善作用最显著,随着添加Pd含量的进一步增加,对Zr-4合金耐腐蚀性能的改善作用减弱。在Zr-4合金中Pd元素以Zr2(Fe,Cr,Pd)、Zr2(Pd,Fe)形式的第二相析出,其中Zr2(Pd,Fe)第二相尺寸较大。固溶在α-Zr中的Pd和尺寸较小的Zr2(Fe,Cr,Pd)型第二相可以提高Zr-4合金的耐腐蚀性能;析出尺寸较大的Zr2(Pd,Fe)第二相后会对Zr-4合金的耐腐蚀性能产生不利的影响。

 

关键字: 锆合金;Zr-4合金;耐腐蚀性能;氧化膜

Effect of Pd addition on corrosion resistance of Zr-4 alloy in LiOH solution
ZHANG Jin-long1,2, LIANG Nan1,2, ZHAO Han-pei1,2, GOU Shao-qiu1,2, YAO Mei-yi1,2, ZHOU Bang-xin1,2

1. Laboratory for Microstructures, Shanghai University, Shanghai 200444, China;
2. Institute of Materials, Shanghai University, Shanghai 200072, China

Abstract:The corrosion resistance of Zr-4 alloy with Pd addition in 0.01 mol/L LiOH solution at 360 ℃ and 18.6 MPa was studied by autoclave test. The microstructures of the alloys and oxide layers were investigated by TEM and SEM. The results show that the corrosion resistance of Zr-4 alloy in LiOH solution is markedly improved with the addition of 0.05%-0.2% Pd. And the Zr-4 alloy with the addition of 0.1%Pd shows the best corrosion resistance. The role of improving the corrosion resistance of Zr-4 alloy weakens when the Pd content further increases. The alloying element of Pd is precipitated as the second phase particles (SPPs) of Zr2(Fe,Cr,Pd) and Zr2(Pd,Fe) in Zr-4 alloys. The SPPs of Zr2(Pd,Fe) are comparably coarse. The solid solution of Pd in α-Zr matrix and the precipitates of fine SPPs of Zr2(Fe,Cr,Pd) are beneficial to improve the corrosion resistance of Zr-4 alloy, while the coarse SPPs of Zr2(Pd,Fe) are harmful to the corrosion resistance.

 

Key words: zirconium alloy; Zr-4 alloy; corrosion resistance; oxide film

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com