超声驻波作用下Al-20%Si合金的微观组织演变
王红玲,乐启炽,张志强,崔建忠,张向文

(东北大学 材料电磁过程研究教育部重点实验室,沈阳 110819)

摘 要: 采用超声驻波处理Al-20%Si合金熔体,研究不同超声驻波处理功率下Al-20%Si合金的微观组织演变,探讨超声驻波对Al-20%Si合金凝固过程的作用和组织细化的机理。结果表明:超声驻波能抑制初晶硅的析出,但声辐射力的作用使已析出的初晶硅偏聚长大;超声驻波处理能实现共晶硅“片状-纤维状”明显的形态转变,凝固后共晶硅转变为频繁分支细小的纤维状;超声功率越大,共晶硅“片状-纤维状”的形态转变越明显;超声驻波可以用于亚共晶Al-Si合金的变质处理中。

 

关键字: Al-20%Si合金;超声驻波;微观组织演变

Microstructure evolution of Al-20%Si alloy with ultrasonic standing wave treatment
WANG Hong-ling, LE Qi-chi, ZHANG Zhi-qiang, CUI Jian-zhong, ZHANG Xiang-wen

Key Laboratory of Electromagnetic Processing of Materials, Ministry of Education,
Northeastern University, Shenyang 110819, China

Abstract:A hypereutectic Al-20%Si alloy was treated by ultrasonic standing wave and the microstructure evolution of Al-20%Si alloy was studied under different ultrasonic powers. The course of crystallization and mechanism of microstructural refinement for the ultrasonic treated alloy were also discussed. The results show that the precipitation of primary silicon is inhibited while the segregation and growth of primary silicon are promoted because of acoustic radiation force under the ultrasonic standing waves treatment. The morphology of eutectic Si is obviously changed after ultrasonic standing wave treatment, varying from flake to fiber shape. Eutectic Si is changed into fine fiber shape with many branches. With the increase of ultrasonic power, the morphological change of eutectic Si from flake to fiber shape is more obvious. Ultrasonic standing wave can be used in the modification of hypoeutectic Al-Si alloy.

 

Key words: Al-20%Si alloy; ultrasonic standing wave; microstructure evolution

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com