中国有色金属学报(英文版)
Transactions of Nonferrous Metals Society of China
Vol. 24 No. 1 July 2014 |
(1. Department of Nanomechatronics Engineering, Pusan National University,
50 Cheonghak-ri, Miryang, Gyeongnam 627-706, Korea;
2. Department of Materials Science and Engineering, Korea National University of Transportation,
Chungju, Chungbuk 380-702, Korea)
Abstract:The nanocrystalline Ho3+/Tm3+/Yb3+ co-doped CaWO4 upconversion (UC) phosphors were successfully synthesized by a modified citrate complex method using microwave irradiation. The citrate complex precursors were heat-treated at temperature ranging from 300 to 700 °C for 3 h. Crystallization of the Ho3+/Tm3+/Yb3+ co-doped CaWO4 was detected at 400 °C, and entirely completed at 600 °C. The Ho3+/Tm3+/Yb3+ co-doped CaWO4 heat-treated at 600 °C showed primarily spherical and homogeneous morphology. Under the laser excitation of 980 nm, Ho3+/Tm3+/Yb3+ co-doped CaWO4 shows the bright white upconversion (UC) emission visible to the naked eye, which is composed of a blue emission at 475 nm from Tm3+, and green and red emissions at 543 and 651 nm respectively from Ho3+. The coordinates of Ho3+/Tm3+/Yb3+ co-doped CaWO4 in the Commission International De’eclairage (CIE) chromaticity diagram could be controlled from a cool to a warm white color depending on the Tm3+ and Ho3+ concentrations. The UC luminescent properties on Tm3+ and Ho3+ concentrations and related mechanism based on laser pump power were discussed in detail.
Key words: upconversion; CaWO4; microwave irradiation; white luminescence