Microstructure of stir zone in dissimilar friction stir welds ofAA6061-T6 and AZ31 alloy sheets
Kwang-Jin LEE, Eui-Pyo KWON

Convergence Components & Agricultural Machinery Application Center,
Korea Institute of Industrial Technology, Jeonju, Korea

Abstract:This study was performed to investigate microstructure of dissimilar friction stir welds manufactured with AA6061-T6 and AZ31 alloy sheets. Dissimilar butt joints were fabricated under the ‘off-set’ condition that tool plunge position shifted toward AZ31 from the interface between AA6061-T6 and AZ31. Optimized tool rotating speed and its traveling speed were selected through a lot of preliminary experiments. Electron back-scatter diffraction (EBSD) technique was applied to measure texture in the stir zone (SZ). Grain size distribution and misorientation angle distribution were also obtained. A remarkably fine-grained microstructure was observed in the SZ. Randomized or weaker plane orientations were formed in the SZ of AA6061-T6, while rotated basal plane orientations were concentrated in the SZ of AZ31. Average size of recrystallized grains was measured as just 2.5-4.5 μm. The fraction of high-angle boundary in the SZ of AA6061-T6 increased and that of low-angle boundary in the SZ of AZ31 decreased compared with the base metals.

 

Key words: AA6061-T6 alloy; AZ31 alloy; friction stir welding; microstructure

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com