不同工艺参数对离心铸造Al-9Ni-15Si复合材料组织与性能的影响
林雪冬1,吕循佳2,刘昌明3

(1. 重庆工程职业技术学院 机械工程学院,重庆 400037;
2. 徐工集团 工程机械股份有限公司,徐州 221004;
3. 重庆大学 材料科学与工程学院,重庆 400030
)

摘 要: 采用离心铸造方法在不同工艺条件下制备Al-9Ni-15Si复合材料筒状零件,研究不同工艺成形铸件沿径向方向和垂直于轴向方向的微观组织特征,测试不同工艺成形铸件的硬度及耐磨性能。结果表明:Al-9Ni-15Si复合材料铸件形成了外层聚集了大量自生初生Al3Ni/Si颗粒、内层含有较多的初生Si/Al3Ni颗粒以及中间层不含颗粒的3层组织。随着浇注温度和模具温度的升高,铸件外、内层颗粒的体积分数逐渐增加,其硬度值逐渐增大,而体积磨损量逐渐减少。在离心场中,Al3Ni的离心运动和Si的向心漂移是形成Al-9Ni-15Si复合材料3层组织的主要原因;而浇注温度和模具温度越高,合金的凝固时间越长,越有利于形成高体积分数的颗粒偏聚区,从而提高复合材料的力学性能。

 

关键字: Al-9Ni-15Si复合材料;初生Al3Ni/Si;硬度;耐磨性;离心铸造;显微组织;性能

Effects of various processing parameters on microstructures and properties of Al-9Ni-15Si composites fabricated by centrifugal casting
LIN Xue-dong1, Lü Xun-jia2, LIU Chang-ming3

1. College of Mechanical Engineering, Chongqing Vocational Institute of Engineering, Chongqing 400037, China;
2. Xuzhou Construction Machinery Group, Construction Machinery Co., Ltd., Xuzhou 221004, China;
3. College of Materials Science and Engineering, Chongqing University, Chongqing 400030, China

Abstract:The Al-9Ni-15Si composite tubes were prepared under different conditions by centrifugal casting. Along the radial direction and the direction perpendicular to the axial direction of the castings, the microstructure characteristics were investigated, and their hardness and wear resistance were measured. The results show that Al-9Ni-15Si composite castings form a three-layer microstructure including a large number of in-situ primary Al3Ni/Si particles in the outer layer, many primary Si/Al3Ni particles in the inner layer and few particles in the middle layer. As the pouring and mould temperatures increase, the particle volume fractions of the outer and inner layers gradually increase, the hardness values on those zones increase as well, while the volume frictions of them gradually reduce. In the centrifugal field, the centrifugal movement of Al3Ni and the centripetal drift of Si are the main reasons for the formation of the Al-9Ni-15Si composite with three layers. The higher the pouring and mold temperatures are, the longer the solidification time is, and the more beneficial to the formation of high volume fraction particle area is, thus improving the mechanical properties of the composite.

 

Key words: Al-9Ni-15Si composite; primary Al3Ni/Si; hardness; wear resistance; centrifugal casting; microstructure; property

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com