高应变速率轧制ZK60板材的超塑性行为
郑 翊1, 2,严红革1, 2,陈吉华1, 2,余海洋1, 2,苏 斌1, 2

(1. 湖南大学 材料科学与工程学院,长沙 410082;
2. 湖南大学 喷射沉积技术及应用湖南省重点实验室,长沙 410082
)

摘 要: 研究高应变速率轧制ZK60镁合金板材在523~673 K、1×10-3~1×10-1 s-1初始应变速率下的超塑变形行为及其特征。研究发现:轧制态ZK60板材在648 K、1×10-3 s-1拉伸时,可获得最大伸长率650%,应变速率敏感性指数高达0.53;在623 K、1×10-2 s-1拉伸时,可获得伸长率584.5%,应变速率敏感性指数为0.47,呈现出较好的高应变速率超塑性。微观组织与理论分析表明:ZK60合金板材在高应变速率下的超塑性变形过程中主要的变形机制为晶界滑移机制(GBS),主要协调机制为晶界扩散控制的位错蠕变,同时还伴有一定程度的液相辅助协调机制。

 

关键字: ZK60镁合金;高应变速率超塑性;高应变速率轧制;细晶镁合金

Superplasticity behavior of ZK60 alloy sheet prepared by high strain rate rolling process
ZHENG Yi1, 2, YAN Hong-ge1, 2, CHEN Ji-hua1, 2, YU Hai-yang1, 2, SU Bin1, 2

1. College of Materials Science and Engineering, Hunan University, Changsha 410082, China;
2. Hunan Provincial Key Laboratory of Spray Deposition Technology and Application, Hunan University,
Changsha 410082, China

Abstract:The superplastic deformation characteristics of the high strain rate rolling ZK60 magnesium alloys at temperature ranging from 523 K to 673 K and at an initial strain rates ranging from 1×10-3 s-1 to 1×10-1 s-1 were investigated. The results show that the maximum elongation to failure of 650% is obtained at 648 K and the strain rate of 1×10-3 s-1 in the as-rolled ZK60 magnesium alloys and its strain rate sensitivity (m) is high up to 0.53. An excellent high strain rate superplasticity with the elongation to failure of 584.5% is obtained at 623 K and the strain rate of 1×10-2 s-1 and its strain rate sensitivity (m) is 0.47. The microstructure and theoretical analysis shows that, at temperature above 573 K, the dominant deformation mechanism in high strain rate superplasticity is grain boundary sliding (GBS), which was studied systematically. The dislocation creep controlled by grain boundary diffusion was considered the main accommodation mechanism, and high strain rate superplasticity was also accompanied by a certain degree of inter-granular liquid phase aiding mechanism, which was observed.

 

Key words: ZK60 magnesium alloy; high strain rate superplasticity; high strain rate rolling; fined grain magnesium alloy

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com