Structural and mechanical properties of CuZr/AlN nanocomposites
Man GU1,2, Yu-cheng WU1,3, Ming-hua JIAO3,4, Xin-min HUANG1

1. School of Materials and Engineering, Hefei University of Technology, Hefei 230009, China;
2. Department of Mechanical Engineering, Hefei University, Hefei 230022, China;
3. Engineering Research Center of Powder Metallurgy of Anhui Province, Hefei 230009, China;
4. Institute of Tribology, Hefei University of Technology, Hefei 230009, China

Abstract:Powder metallurgy method was used to prepare copper alloy nanocomposites (CuZr/AlN) with high strength and conductivity. Optical microscopy, high-resolution transmission electron microscopy and other methods were adopted to study the impact of different sintering technologies on the structural and mechanical properties as well as the impact of solution and aging treatments on the mechanical properties of CuZr/AlN. The result shows that the specimen has a dense structure, and the size of the crystal grain is around 0.2 μm. The Brinell hardness of the specimen increases with the increase in re-pressing pressure and sintering temperature. The Brinell hardness of specimen also increases with the increase in zirconium content. However, above 0.5% (mass fraction) of zirconium content, the Brinell hardness of the nanocomposites is reduced. The buckling strength of the specimens increases with the increase in re-pressing pressure and sintering temperature. The buckling strength is the highest when the zirconium content is 0.5%. The Brinell hardness is lower after solution and aging treatments at 900 °C. The Brinell hardness of the CuZr/AlN series specimen after the aging treatment at 500 °C or 600 °C increases. The specimen was also over aged at 700 °C.

 

Key words: CuZr/AlN nanocomposites; powder metallurgy; mechanical properties

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com