Microstructures of TC21 alloys after hydrogenation and dehydrogenation
Xiao-li WANG1, Yong-qing ZHAO2, Xiao-wei WEI1, Hong-liang HOU3

1. School of Material Science and Engineering, Xihua University, Chengdu 610039, China;
2. Northwest Institute for Nonferrous Metal Research, Xi’an 710016, China;
3. Beijing Aeronautical Manufacturing Technology Research Institute, Beijing 100024, China

Abstract:Microstructural evolution and phase transformation of hydrogenated and dehydrogenated TC21 alloys were investigated by optical microscopy (OM), X-ray diffraction (XRD) and transmission electron microscopy (TEM). XRD peaks of α and β phases after hydrogenation shifted to low angle because of lattice expansion with the solution of hydrogen atoms. Microstructure of TC21 alloy after hydrogenation changed apparently. Compared to the as-received one, the contrasts of equiaxed α phase and transformed β phase under optical microscope were reversed. In addition, XRD and TEM analyses revealed that hydrides and α′ martensite precipitated from α and β phases. Bulk of twins and some Ti3Al particles were observed in hydrogenated TC21 alloy, which means that hydrogen led to the redistribution of alloying elements in α and β phase. After dehydrogenation, the microstructure of TC21 alloy was similar to that of the as-received one, which consisted of α and β phases.

 

Key words: δ hydride; Ti3Al phase; α′ martensite; twin

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com