Mechanical and metallurgical properties of dissimilar friction stir welded AA5083-H111 and AA6351-T6 aluminum alloys
R. PALANIVEL1, P. KOSHY MATHEWS2, I. DINAHARAN3, N. MURUGAN4

1. Department of Mechanical Engineering, Roever College of Engineering and Technology,
Perambalur, 621212, Tamil Nadu, India;
2. Department of Mechanical Engineering, Kalaivani College of Technology, Coimbatore, 641105, Tamil Nadu, India;
3. Department of Mechanical Engineering, V V College of Engineering, Tisaiyanvilai, 627657, Tamil Nadu, India;
4. Department of Mechanical Engineering, Coimbatore Institute of Technology,
Coimbatore, 641014, Tamil Nadu, India

Abstract:The microstructure and mechanical characterization of dissimilar friction stir welded AA5083-H111 and AA6351-T6 aluminum alloys were studied. Three different welding speeds (36, 63 and 90 mm/min) were used to weld the dissimilar alloys. The effect of welding speed on mechanical and metallurgical properties was analyzed. It is found that the welding speed of 63 mm/min produces better mechanical and metallurgical properties than other welding speeds. The weld zone is composed of three kinds of microstructures, namely unmixed region, mechanically mixed region and mixed flow region. The fracture mode was observed to be a ductile fibrous fracture.

 

Key words: aluminum alloys; friction stir welding; welding speed; tensile strength; microstructure

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com