AZ31镁铝合金铈盐转化膜的致密化处理
徐洛民,王 昕,雷 黎,左 轲

(中国海洋大学 材料科学与工程研究院,青岛 266100)

摘 要: 采用磷酸盐对AZ31镁铝合金铈转化膜进行致密化处理,利用扫描电镜(SEM)、X射线光电子能谱(XPS)和电化学方法等对致密化处理之后的膜层性能进行表征,探讨转化膜致密化处理的作用机理。结果表明:转化膜经过致密化处理之后,膜表层裂纹减少,致密性得到改善,提高了对基体的覆盖度,在NaCl溶液中的耐腐蚀性能提高。转化膜中Ce4+的含量减少,部分铈的氧化物/氢氧化物转变为CePO4,降低了膜层中结晶水的含量,减少了裂纹的产生与发展,提高了膜层的性能。

 

关键词: 镁合金;转化膜;后处理;裂纹;腐蚀

Densification process of cerium-based conversion coatings on AZ31 magnesium alloy
XU Luo-min, WANG Xin, LEI Li, ZUO Ke

Institute of Materials Science and Engineering, Ocean University of China, Qingdao 266100, China

Abstract:The densification process of cerium-based conversion film on AZ31 magnesium alloy was achieved by phosphate. The properties of the film and the densification mechanism were investigated exhaustively by scanning electronic microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and electrochemical methods. The results reveal that after the post-treatment the denseness of the cerium-based conversion coatings is improved, which benefits a lot from the reduced number of cracks. As a result, the corrosion resistance of the conversion film in NaCl solution is strengthened. The less Ce4+ ion, the transformation of hydrated cerium oxides to stable CePO4 and lower crystal water content in the films attribute to the reduce of the crack number and the improvement of the film performance.

 

Key words: magnesium alloys; conversion coatings; post-treatment; crack; corrosion

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com