中国有色金属学报(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 23 No. 10 October 2013 |
（1. Faculty of Materials Science and Engineering,
Kunming University of Science and Technology, Kunming 650093, China;
2. National Local Joint Engineering Laboratory of Engineering Applications of Microwave Energy and
Equipment Technology, Kunming University of Science and Technology, Kunming 650093, China;
3. Key Laboratory of Unconventional Metallurgy, Ministry of Education,
Kunming University of Science and Technology, Kunming 650093, China;
4. Chemical Engineering Department, The Petroleum Institute, P.O. Box 2533, Abu Dhabi, United Arab Emirates）
Abstract:A novel synthesis method of carbon-coated LiNi1/3Mn1/3Co1/3O2 cathode material for lithium-ion battery was reported. The carbon coating was produced from a precursor, glucose, by microwave-pyrolysis method. The prepared powders were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray fluorescence (XRF) and charge/discharge tests. XRD results indicate that the carbon coating does not change the phase structure of LiNi1/3Mn1/3Co1/3O2 material. SEM results show that the surface of spherical carbon-coated material becomes rough. Electrochemical performance results show that the carbon coating can improve the cycling performance of LiNi1/3Mn1/3Co1/3O2. The specific discharge capacity retention of the carbon-coated LiNi1/3Mn1/3Co1/3O2 reached 85.0%-96.0% at the 50th cycle at 0.2C rate, and the specific discharge capacity retention is improved at a high rate.
Key words: lithium-ion battery; cathode material; carbon coating; microwave pyrolysis method; electrochemical performance