磁场对厚板Ti-6Al-4V合金窄间隙TIG焊缝组织的影响
孙清洁1,郭 宁1,胡海峰2,冯吉才1

(1. 哈尔滨工业大学(威海) 山东省特种焊接技术重点实验室,威海 264209;
2. 苏州热工研究院,苏州 215004
)

摘 要: 对56 mm厚Ti-6Al-4V合金进行窄间隙磁控电弧TIG焊接,通过金相显微镜对接头各区组织进行对比分析。结果表明:在窄间隙的多层单道焊接中,接头各区的组织、结晶形态及生长方向存在很大差异。焊缝区一次结晶组织为表层焊道上表面的柱状粗大组织及熔合线附近、焊道内部的等轴晶组织。熔合线处,电磁作用提高了平面状结晶前沿及后来形成的等轴晶的稳定性,最终随着磁场强度的增加在熔合线附近逐渐由柱状晶转变为等轴晶。焊缝中心处,磁控电弧作用使得生成的等轴晶稳定性提高,随着磁场强度的增加,等轴晶逐渐单方向伸长,在热传导方向上,即焊缝表层垂直方向生成粗大的柱状晶。

 

关键字: Ti-6Al-4V合金;磁场;窄间隙焊接;焊缝组织

Effect of magnetic field on weld structure of large thickness Ti-6Al-4V alloy with narrow-gap TIG welding method
SUN Qing-jie1, GUO Ning1, HU Hai-feng2, FENG Ji-cai1

1. Shandong Provincial Laboratory of Special Welding Technology, Harbin Institute of Technology at Weihai,
Weihai 264209, China;
2. Suzhou Nuclear Power Research Institute, Suzhou 215004, China

Abstract:A narrow-gap controlling magnetic field TIG welding experiment was conducted directing at the 56 mm-thickness Ti-6Al-4V titanium alloy. Afterwards, an analysis was taken to compare each weld joint microstructure by means of metallographic microscope. The results show that, during the multilayer single channel of narrow gap welding, the joint microstructure, the crystal structure and the growth orientation significantly differ from each other. The first crystal structure in the weld zone is an equiaxed grain which shows a columnar coarse grain at the top layer of the weld surface and near the bond line and the internal weld. Since the electromagnetic effect improves the stability of flat crystal and the equiaxed grains appear afterwards, ultimately, there are equiaxed grains translated from coarse columnar grains in the front of bond line with the magnetic field strength increasing. Due to the effect of magnetic controlled arc on improving the stability of equiaxed grains, along with the magnetic field strength increasing, the equiaxed grains gradually extend in a single direction; in the direction of heat conduction, i.e., in the vertical direction of the weld surface, the coarse columnar grains generate.

 

Key words: Ti-6Al-4V alloy; magnetic field; narrow-gap welding; weld microstructure

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com