中国有色金属学报(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 23 No. 8 August 2013 |
（1. School of Chemistry and Chemical Technology, Shanghai Jiao Tong University, Shanghai 200240, China;
2. School of Materials Science and Engineering, Central South University, Changsha 410083, China;
3. Department of Chemistry, Zhejiang University, Hangzhou 310027, China）
Abstract:The electrodeposition and characterization of nano-structured black nickel coatings were presented. The influences of bath pH, electrodeposition time, stirring speed, temperature and current density on the color and microstructure of the electrodeposited nickel film were investigated through naked eyes, scanning electron microscopy (SEM) and X-ray diffraction (XRD) techniques. Meanwhile, the corrosion resistance of the optimized black nickel film was evaluated by the polarization measurement and electrochemical impedance spectroscopy (EIS) in the neutral 3.5% NaCl solution. The results show that the color of the electrodeposited nickel film was highly dependent on the above technological parameters. The operating parameters were optimized mainly according to the color. The optimized black nickel film possesses nano-structure with an average grain diameter of about 50 nm. It also exhibits enhanced corrosion resistance when compared with white nickel coatings electrdodeposited under the same condition except the variation of the electroplating current density.
Key words: electrodeposition; nano-black nickel film; corrosion