电磁搅拌下混合稀土对半固态A356合金初生α相的细化机理
刘 政1,许鹤君2,罗浩林2,周志鹏2,谌庆春2

(1. 江西理工大学 机电工程学院,赣州 341000;
2. 江西理工大学 材料科学与工程学院,赣州 341000
)

摘 要: 为获得细小、圆整且分布均匀的半固态A356合金初生α相,向合金熔体中添加了不同含量的混合稀土La和Ce对合金进行变质处理,熔体经620 ℃浇注后,利用变频控制的电磁搅拌装置对熔体进行电磁搅拌15 s并使其在610 ℃保温10 min,观察并分析合金凝固组织中初生α相的形貌与尺寸。利用扫描电镜和能谱仪分析测定La和Ce在基体的分布情况,探讨混合稀土元素在电磁搅拌条件下对初生α相的细化机制。结果表明:La和Ce在电磁搅拌条件下易于均匀分布在初生α相周围,混合稀土元素La与Ce在短时弱电磁搅拌的条件下可以高效地细化半固态A356合金组织,稀土对半固态A356铝合金的初生α相细化机制与稀土在铝合金中产生的共晶反应有关。

 

关键字: 混合稀土;半固态A356合金;电磁搅拌;初生α相;共晶反应

Refinement mechanism of mixed rare earth on primary α phase in semisolid A356 alloy under electromagnetic stirring
LIU Zheng1, XU He-jun2, LUO Hao-lin2, ZHOU Zhi-peng2, CHEN Qing-chun2

1. Faculty of Mechanical and Electrical Engineering, Jiangxi University of Science and Technology,
Ganzhou 341000, China;
2. Faculty of Materials Science and Engineering, Jiangxi University of Science and Technology,
Ganzhou 341000, China

Abstract:In order to obtain the fine, round and uniform distribution primary α phase in semisolid A356 alloy, the different amounts of mixed RE elements La and Ce were added into the alloy melt,and the melt was poured at 620 ℃ and slightly electromagnetically stirred for 15 s with an electromagnetic stirrer controlled by frequency conversion, then, it was isothermally held at 615 ℃ for 10 min. The morphology and size of the primary α phase were analyzed, and the distributions of La and Ce were researched by SEM and EDS. The refinement mechanism of mixed RE under electromagnetic stirring was discussed. The results indicate that RE elements La and Ce are easy to uniformly distribute around the primary α phase under electromagnetic stirring, and RE elements La and Ce can effectively refine the primary α phase under the condition of short and weak electromagnetic stirring. The refining mechanism of RE on the primary α phase in semisolid A356 alloy can be concerned with the eutectic reaction induced by RE in the alloy.

 

Key words: mixed rare earth; semisolid A356 alloy; electromagnetic stirring; primary α-Al phase; eutectic reaction

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com