薄壁铝合金压铸充型沿程的组织与力学性能
朱必武1, 2,李落星1, 2,刘  筱1, 2,王水平1, 2,张立强1, 2

(1. 湖南大学 汽车车身先进设计与制造国家重点实验室,长沙 410082;
2. 湖南大学 机械与运载工程学院,长沙 410082
)

摘 要: 采用压铸制备薄壁AlSi10MnMg铝合金铸件,用金相技术、密度、拉伸性能等分析方法讨论浇注温度对薄壁铝合金压铸充型沿程的组织与力学性能的影响。结果表明:随着浇注温度的升高,试样流动临界长度增加,气孔增多,α(Al)枝晶变细,抗拉强度和断后伸长率先增加后降低。随着充型沿程流动长度的增加,气孔先减少后增加,α(Al)枝晶变化不大。当浇注温度为650和680 ℃时,试样抗拉强度和断后伸长率沿充型流动长度的增加而减小;当浇注温度为710和740 ℃时,试样抗拉强度和断后伸长率沿充型流动长度的增加变化较小。

 

关键字: 薄壁铝合金;压铸;组织;力学性能

Microstructure and mechanical properties along fluidity length of thin-wall aluminum alloy under high pressure die casting conditions
ZHU Bi-wu1, 2, LI Luo-xing1, 2, LIU Xiao1, 2, WANG Shui-ping1, 2, ZHANG Li-qiang1, 2

1. State Key Laboratory of Advanced Design and Manufacturing for Vehicle Body, Hunan University,
Changsha 410082, China;
2. College of Mechanical and Vehicle Engineering, Hunan University, Changsha 410082, China

Abstract:The thin-wall AlSi10MnMg aluminum alloy samples were prepared by high pressure die casting. The effects of pouring temperature on the microstructure and mechanical properties along the fluidity length were discussed by metallographic techniques, density measurement and tensile tests. The results show that, with the pouring temperature increasing, the critical fluidity length and porosity increase, and α(Al) grain size decreases and the ultimate tensile strength and elongation to fracture increase firstly, and then decrease. With the increase of the fluidity length, the porosity decreases firstly and then increases, but the α(Al) grain size is insignificant. The ultimate tensile strength and elongation to fracture decrease along the fluidity length under pouring temperatures of 650 and 680 ℃. However, the difference of the ultimate tensile strength and elongation to fracture along the fluidity length under pouring temperatures of 710 and 740 ℃ is insignificant.

 

Key words: thin-wall aluminum alloy; high pressure die casting; microstructure; mechanical properties

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com