丝束电极研究镀锌层存在点缺陷的锌/钢电偶腐蚀行为
张大磊1, 王 伟2, 金有海1, 唐 晓1, 李 焰1

(1. 中国石油大学(华东) 机电工程学院,东营  257061;2. 中国海洋大学 化学化工学院,青岛 266100)

摘 要: 采用3种不同配置比例的锌/碳钢异材质丝束电极,模拟镀锌层存在不同大小点缺陷时的热浸镀钢,研究锌/钢电偶在不同腐蚀阶段的电位和电流密度分布。结果表明,在钢丝与锌丝面积比为1׃120、9׃112和25׃96的3种情况下,锌丝均能给钢丝提供足够的阴极保护,且锌丝之间存在明显的电位、电流分布不均现象,主要阳极区先随机地在邻近钢丝的锌丝区域内转移,而后逐渐向远端锌丝扩展;钢丝之间也存在电化学参数分布不均一现象,钢丝在受到保护的同时表面会有氢原子析出,且随着阴、阳极面积比的增大,析氢电流密度逐渐减小。

 

关键字: 丝束电极;镀锌层;电偶腐蚀;阴极保护;氢析出

Wire beam electrode technique for investigating galvanic corrosion behavior of galvanized steel−spot defect
ZHANG Da-lei1, WANG Wei2, JIN You-hai1, TANG Xiao1, LI Yan1

1. College of Machinery and Electronic Engineering, China University of Petroleum, Dongying 257061, China;
2. College of Chemistry and Chemical Engineering, Ocean University of China, Qingdao 266100, China

Abstract:Three kinds of wire beam electrodes(WBE) composed of zinc and mild steel wires were developed, which were used to simulate hot-dip galvanized steel with spot coating defect at different dimensions, to obtain the spatial distributions of potential and current density and their variations with time during the galvanic corrosion. The results show that the zinc wires within WBEs can provide enough cathodic protection to steel wires after immersed in seawater, with surface area ratio of zinc wires to steel wires as 1:120, 9:112, and 25:96, respectively. The potential and current density distributions are found to be inhomogeneous among zinc wires; firstly, the main anodic areas shift randomly among the zinc wires adjacent to steel wires, then transfer to the direction away from steel wires, and finally occur on the zinc wires farther. The similar heterogeneous phenomenon also appears on steel wires surface on which hydrogen evolution may take part in the cathodic process occurred. Meanwhile, the current density of water molecule reduction reaction decreases with the ratio of the surface area of steel wires to zinc wires increasing.

 

Key words: wire beam electrode; zinc coating; galvanic corrosion; cathodic protection; hydrogen evolution

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com