摘 要: 采用500~1 000 ℃热循环20次,研究Ti-6Al-4V(TC4)合金性能及微观组织的变化。结果表明:随热循环温度的升高,TC4合金强度先降低后升高;低于800 ℃时,TC4合金塑性随热循环温度升高变化不大,高于800 ℃,随热循环温度升高,TC4合金塑性快速降低;随温度升高,TC4合金的晶粒明显长大,温度高于800 ℃时,TC4合金中开始形成片层状组织,至1 000 ℃时,合金组织几乎呈全片层状。
关键字: TC4钛合金;热循环;力学性能;微观组织
and mechanical properties of Ti-6Al-4V alloy
(1. Northwest Institute for Nonferrous Metal Research, Xi’an 710016, China;
2. School of Materials Science and Engineering, Xi’an Jiaotong University, Xi’an 710049, China)
Abstract:The changes of microstructures and mechanical properties of Ti-6Al-4V alloy after thermal cycling 20 times from 500 ℃ to 1 000 ℃ were researched. The results show that the strength of Ti-6Al-4V alloy firstly reduces and then increases with the increase of cycling temperature. If the cycling temperature is lower than 800 ℃, its plasticity changes less with the temperature. While the temperature is higher than 800 ℃, its plasticity decreases fast. The grain size grows fast with increasing temperature. While the temperature is over 800 ℃, the lamellar microstructure forms, when the temperature reaches 1 000 ℃, the microstructure is almost lamellar one.
Key words: Ti-6Al-4V alloy; thermal cycling; mechanical properties; microstructures