(中南工业大学材料科学与工程系,长沙410083)
摘 要: 采用正交试验法研究了热轧复合工艺(包括加热温度、保温时间、热轧复合总加工率和道次加工率分配方式)对界面结合强度的影响,并应用金相显微镜及扫描电镜(SEM)分析了界面的结合特性,确定了高阻尼铝合金层压板热轧复合的较优工艺:热轧复合加热温度350℃,保温时间1h,总轧制加工率75%,第一、二道次加工率之和为35%左右。热轧复合板的界面结合为冶金结合。
关键字: 阻尼材料 热轧复合 结合强度 界面特性
INTERFACIAL CHARACTERISTICS OF HIGH
DAMPING LAMINATE ALUMINIUM ALLOY SHEET
(Department of Materials Science and Engineering,
Central South University of Technology, Changsha 410083)
Abstract:The hot-roll bonding is a key procedure to produce high damping laminate aluminium alloy sheets. The influences of hot-roll bonding technologies involving heating temperature, holding time, total reduction ratio and reduction ratio per operation on interfacial bonding strength of various layers in the composite were studied by means of orthogonal test method. The interfacial characteristics between various bonding layers were analysed with metalloscope and scanning electron microscope. The optimum technologies for manufacturing hot-roll bonding high damping laminate aluminium alloy sheets were determined, that is, heating temperature 350℃, holding time 1 h, total reduction ratio 75%, summary reduction ratio of the first and second operations 35%.
Key words: damping materials hot-roll bonding bonding strength interfacial characteristic