(哈尔滨工业大学材料科学与工程学院,哈尔滨 150001
哈尔滨汽轮机责任有限公司,哈尔滨 150012)
摘 要: 研究了喷射成形Al93.5Cu3Fe1.5Ni1Ce0.5Zr0.5合金快速凝固组织特征及弥散强化相的形成。结果表明,喷射成形快速凝固技术显著地细化了合金组织;预成形毛坯具有3 种典型的组织特征,其中主要弥散强化相为具有立方晶体结构、晶格常数a=0.852 nm 的Al17Cu4FeNiCe相
关键字: 快速凝固 喷射成形 高强铝合金 微观组织
(College of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, P. R. China
Harbin Steamer Plant Co. Ltd., Harbin 150012, P. R. China)
Abstract:The characteristic microstructures and formation of dispersoid of spray formed Al93.5Cu3Fe1.5Ni1Ce0.5Zr0.5 alloy were investigated. The observation results showed that the microstructures of deposit are fine and homogeneous and there exist three kinds of typical formation mechanisms of microstructures in deposit. The main dispersoid in deposit is AAl17Cu4FeNiCe phase with complicated cubic crystal structure whose lattice constant keeps 0.852 nm.
Key words: rapid solidification; spray forming; high-strengthened aluminium alloy; microstructure