工艺参数对TiAl合金激光表面合金化改性层组织与耐磨性的影响
何秀丽, 王华明

(北京航空航天大学 材料科学与工程系, 北京 100083)

摘 要:   利用元素氮和元素碳对 γ TiAl合金(简称TiAl合金)进行激光表面合金化处理,分别制得了以TiN及TiC硬质耐磨相为增强相的快速凝固原位耐磨复合材料表面改性层,改性层与基体间为完全的冶金结合,其显微组织从熔池底部到自由表面具有梯度渐变特征,越接近自由表面,增强相越密集。较系统地研究了激光表面合金化工艺参数对改性层显微组织以及在磨料磨损及滑动磨损条件下耐磨性能的影响。激光束扫描速度越低,表面改性层增强相体积分数越高,材料显微硬度提高越多,耐磨性越强。

 

关键字:  γ TiAl合金; 激光表面合金化;耐磨性

Effects of processing parameters on microstructure and wearresistance of laser surface alloyed layer on TiAl alloy
HE Xiuli, WANG Huaming

Department of Materials Science and Engineering,Beijing University of Aeronautics and Astronautics,Beijing 100083, P.R.China

Abstract:Laser surface alloying with nitrogen and carbon were employed to produce modified layers on TiAl alloy. The rapidly solidified insitu composites layers reinforced by titanium nitride and titanium carbide were gained respectively, and the interfaces between the layers and substrate were metallurgic bonds. From bottom of molten bath to free surface, there was gradient change characteristic in microstructures. The nearer the free surface, the higher the volume fraction of reinforced phase. The effects of laser processing parameters on microstructures and wear resistance of surface alloyed layer were studied. With decreasing laser beam scanning rate, the volume fraction of reinforced phase increases, the microhardness of the samples increases and the wear resistance is improved.

 

Key words: γ TiAl intermetallics; laser surface alloying; wear resistance

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com