摘 要: 研究了不同含量的磷在IN718合金中的作用。结果表明,磷对持久和蠕变性能有显著的影响,可提高IN718合金晶界抗蠕变开裂的能力。将磷含量由0.003%提高至0.03%,持久寿命先是增加而后降低,并在含磷0.025%处达到持久寿命峰值。磷对应力指数影响不大,但对表观蠕变激活能影响显著。磷的有益作用主要来自于抑制晶界扩散和改善晶界δ相。
关键字: IN718合金; 磷; 晶界; 扩散; 持久性能;蠕变
(Institute of Metal Research, The Chinese Academy of Sciences, Shenyang 110015, P.R.China)
Abstract:The effect of phosphorus on IN718 alloy was studied. The results showed that phosphorus can significantly affect the stressrupture properties. With increasing content of phosphorus from 0.003% to 0.03%, the stressrupture life increases firstly and then decreases and reaches the peak value at 0.025%. Phosphorus does not appears to modify the stress exponent but influences the apparent activation energy for creep markedly. The beneficial effects of phosphorus mainly arise from the suppression of diffusion along grain boundary and the improvement of grain boundaryδphase.
Key words: IN718 alloy; phosphorus; grain boundaries; diffusion; stress-rupture test; creep