润滑剂对高纯铝形变织构的影响
张新明, 蒋红辉, 肖亚庆, 陈志永, 刘楚明, 周卓平

(中南大学 材料科学与工程系, 长沙 410083)

摘 要:  采用ODF法研究和分析了润滑剂对高纯铝冷轧形变织构的影响,揭示了两种润滑条件下形变织构的演变规律。结果表明:大冷轧变形程度下,采用机油润滑,形变织构为典型的面心立方金属的轧制织构,即由强的 B-、Cu-及S-织构组分构成,而且取向分布的密度峰值处在 S 取向位置;煤油润滑时轧制织构相对较弱,但Cu织构最强,同时产生了明显的剪切织构{001}〈110〉(Rot.Cube-织构)。采用机油润滑时,轧制变形比较均匀。低变形轧制时晶粒取向聚集于α线,随变形量增加,向β线取向聚集,最终形成铜型轧制织构;而煤油粘度小,轧制过程中接触表面摩擦系数较大,不均匀变形严重,低轧制程度时发现有表面剪切Rot.Cube-织构, 随着塑性变形增加,Rot.Cube-织构逐渐向Cu-取向转化;变形至95%后,随着变形程度增加,S-织构减弱。

 

关键字: 高纯铝; 形变织构; 剪切织构; 润滑

Influence of lubricants on
deformation textures in high purity Al
ZHANG Xin-ming, JIANG Hong-hui, XIAO Ya-qing,
CHEN Zhi-yong, LIU Chu-ming, ZHOU Zhuo-ping

Department of Materials Science and Engineering,
Central South University, Changsha 410083, P.R.China

Abstract:The influence of the cold rolling lubricants on the deformation texture in high purity Al was investigated in detail by ODF 's. The results show that the foil which is deformed at room temperature at high reduction with machine oil lubrication has developed the typical rolling textures of FCC metals, which consist of B-, Cu- and S-component, and the maximum peak of the orientation density f (g)trends towards S position; in the case of the kerosene lubricant, however,  the rolling textures were comparatively weak, and at the same time the shear texture {001}〈110〉is developed. The rolling deformation was much more homogeneous and the shear strain was lower on the condition of machine oil lubricant because of its high viscosity. The grain orientations gathered around α-fibre at low reduction and shifted towards β-fibre with increasing reduction. At high reduction the final texture became the coppertype rolling texture of FCC metals. Comparatively, the viscosity of kerosene is much lower, the coefficient of friction between the roller and the metal surface is higher during rolling, and it results in the inhomogeneous deformation. At lower reduction the shear texture(Rot.Cube texture) in the rolled surface of the foil appeared,  the Rot. Cube-orientation shifted towards Cu orientation with increasing reduction.

 

Key words:  high purity aluminum; deformation texture;shear texture; lubrication

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com