纳米TiO2的燃烧合成及其光催化性能
于永丽1, 翟秀静2, 符  岩2,姚广春2

( 1. 东北大学 理学院, 沈阳 110004;
| 2. 东北大学 材料冶金学院, 沈阳 110004
)

摘 要: 以TiOSO4为原料, 加入燃烧剂,采用燃烧合成法制备了纳米TiO2;考察了燃烧剂的种类、 燃烧剂的加入量、 pH值、点火温度、 煅烧时间等对产物的影响; 以甲基橙溶液为实验对象, 研究了该TiO2的光催化性能。结果表明: 以柠檬酸为燃烧剂, 当TiO(NO3)2和柠檬酸的摩尔比为9∶15, 溶液pH>5, 点火温度为550℃时合成TiO2。 XRD测试表明, 合成产物为单一锐钛矿型, 晶体粒度为14.8nm; TEM测试表明, 产品粒度分布均匀; 当用高压汞灯照射2h时, 甲基橙的降解率为91%。

 

关键字: 二氧化钛; 光催化; 燃烧合成; 纳米

Combustion synthesis of nanosized titania and its photocatalytic activity
YU Yong-li1, ZHAI Xiu-jing2, FU Yan2, YAO Guang-chun2

  1. Science School, Northeastern University, 
Shenyang 110004, China;
2. School of Materials and Metallurgy,
 Northeastern University,Shenyang 110004, China

Abstract: Nanosized titania was synthesized by combustion process by using TiOSO4 as raw material and citric acid as fuel. Preparing conditions were studied, such as fuels, amount of fuels, pH value, ignition temperature, calcinations time, etc. The results show that when molar ratio of Ti to citrate is 9∶15 then pH>5 and ignition temperature is 550℃, TiO2 is prepared. XRD tests show that the products are anatase and the crystallite size is 14.8nm, and TEM tests indicate that the powders are uniform. Photocatalytic activity was carried out. After the solution of cymene orange is illuminated for 2h with UV lamp as light source, degradation efficiency of the solution is 91%.

 

Key words: titania; photocatalytic; combustion synthesis; nanosized

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com