厚铝合金板搅拌摩擦焊塑性金属不同深度的
水平流动状况
王希靖1, 韩晓辉1,2, 李常锋1,包 孔1, 郭瑞杰1

( 1. 兰州理工大学 甘肃省有色金属新材料国家重点实验室,
兰州 730050;
2. 中国南车集团四方机车车辆股份有限公司, 青岛 266031
)

摘 要:  通过在10 mm厚LF2铝合金板的不同位置嵌入示踪Fe粉, 进行搅拌摩擦焊对接实验, 焊后截取不同深度的水平面试样, 采用扫描电镜对试样进行能谱分析, 通过观察Fe粉在焊缝金属中的水平分布, 确定了10 mm厚LF2搅拌摩擦焊焊缝金属的二维水平流动状况。结果表明, 塑性金属流动关于焊缝中心并不对称。 焊缝下部金属受搅拌针作用, 前进侧大部分金属与焊接方向相反向后流动, 小部分金属向前流动, 但都未进入返回侧;返回侧金属都向后流动, 且有部分金属进入前进侧。 焊缝上部金属主要受轴肩作用, 前进侧大部分金属向前流动但未进入返回侧, 小部分金属向后流动; 返回侧金属沿旋转方向流入前进侧。

 

关键字:  搅拌摩擦焊; 流场; 前进侧; 返回侧; 示踪粒子

Horizontal flow status of plastic metal in different depth during friction stir welding for thick aluminum alloy
WANG Xi-jing1, HAN Xiao-hui12, LI Chang-feng1, BAO Kong1, GUO Rui-jie

1. State Key Laboratory of Advanced Non-ferrous Metal Materials,
Gansu Province,Lanzhou University of Technology,Lanzhou 730050,China;
2. Sifang Locomotive & Rolling Stock Ltd.,CSR,Qingdao 266031,China

Abstract: Marker Fe grains were inserted into 10 mm LF2 aluminum alloy in different positions during the friction stir welding course. After butt welding, the samples which were selected in horizontal sections in different depths were analyzed by using EDS(energy dispersive X-ray spectroscopy) of SEM(scanning electron microscope). The 2-D horizontal flow status of friction stir welding for 10 mm LF2 aluminum alloy was confirmed by observing the horizontal distributions of Fe grains in welding zone. The results show that the flow is not symmetric about the weld centerline. The lower metal of weld is completely affected by pin. The bulk of metal in the advancing side is transported backward against the welding direction. However,a small amount is moved forward at the edge of the pin. The metal in the retreating side is only transported against the welding direction and some metal flows into the advancing side. The upper metal of weld is mainly affected by shoulder. The bulk of metal in the advancing side moves forward in the welding direction and a little backward; but no metal flows into the retreating side. However,the bulk of metal in the retreating side is transported backward into the advancing side along the rotation direction. 

 

Key words: friction stir welding;flow field;advancing side;retreating side;marker grain

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com