中国有色金属学报

ZHONGGUO YOUSEJINSHU XUEBAO

第18卷    第4期    总第109期    2008年4月

[PDF全文下载]        

    

文章编号:1004-0609(2008)04-0608-06
新型C/C-TaC复合材料的微观结构及其力学性能
王雅雷,熊 翔,李国栋,肖 鹏,陈招科

(中南大学 粉末冶金国家重点实验室,长沙 410083)

摘 要: 采用化学气相渗透(CVI)法和热固性树脂浸渍-炭化法复合工艺制备含5%TaC的新型C/C-TaC复合材料,并对复合材料的微观结构和力学性能进行了研究。结果表明:C/C-TaC复合材料中TaC以涂层形式均匀致密地包覆在炭纤维周围,形成管状微观结构,大大提高C/C-TaC复合材料试样的平均强度和韧性。复合材料试样平均抗弯强度达到270 MPa,比C/C复合材料的提高近70%;最大断裂位移达到1.2 mm,比C/C复合材料的提高近140%,表现为良好的假塑性断裂。

 

关键字: C/C-TaC复合材料;微观结构;抗弯强度;增强增韧

Microstructures and mechanical properties of novel C/C-TaC composite
WANG Ya-lei, XIONG Xiang, LI Guo-dong, XIAO Peng, CHEN Zhao-ke

State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China

Abstract:The fabrication of new carbon fiber reinforced carbon-tantalum carbide composites with 5% TaC by chemical vapor infiltration(CVI) and impregnation/carbonization of thermosetting phenolic resin was presented. The microstructures and mechanical properties of C/C-TaC composites were investigated. The results show that TaC with form of coating enwrap evenly and compactly around with the carbon fiber in C/C-TaC composites and form the cannular microstructure, both the average strength and toughness of C/C-TaC composites sample increase apparently. The average flexural strength of C/C-TaC composites sample reaches up to 270 MPa, approximately increases by 70% comparing with C/C composites. The maximum fracture displacement reaches 1.2 mm, approximately increases by 140% comparing with C/C composites, which exhibits shearing failure fracture behaviors.

 

Key words: C/C-TaC composites; microstructure; bending strength; reinforcement and plasticization

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com