AZ91D镁合金半固态触变成形压铸工艺
阎峰云1,强旭东2,张玉海1,黄晓锋2,范松岩1

(1. 兰州理工大学 甘肃省有色金属新材料省部共建国家重点实验室,兰州 730050;2. 兰州理工大学 有色金属合金及加工教育部重点实验室,兰州 730050)

摘 要: 采用等温热处理对AZ91D镁合金进行非枝晶化,研究半固态镁合金的触变压铸工艺,得到性能良好的触变压铸镁合金试件。通过改变压力和压射速度等工艺参数,发现其抗拉强度和伸长率都随着压力或速度的上升而增加,当增压压力为35 MPa和压射速度为4.5 m/s时,其抗拉强度达到最大,为237.5 MPa,伸长率为4.8%。通过组织分析认为,半固态触变压铸对晶粒细化效果明显,这与固相颗粒在充型过程中的二次破碎,液相喷射分散后凝固具有直接的关系。

 

关键字: 镁合金;触变成形;半固态压铸;等温处理;力学性能

Die-casting process of semi-solid thixo-forming of AZ91D Mg alloy
YAN Feng-yun1, QIANG Xu-dong2, ZHANG Yu-hai1, HUANG Xiao-feng2, FAN Song-yan1

1. State Key Laboratory of Gansu Advanced Non-ferrous Metal Materials, Lanzhou University of Technology, Lanzhou 730050, China;2. Key Laboratory of Non-ferrous Metal Alloys and Processing, Ministry of Education, Lanzhou University of Technology, Lanzhou 730050, China

Abstract:The non-dendrite or spherical grains microstructure of AZ91D magnesium was obtained using the isothermal treatment technique and the thixo-casting process were studied under semi-solid state. The specimens with good properties were obtained and analyzed. The effects of injection speed and additional pressure on tensile strength, elongation rate and microstructure of specimens were investigated. The results show that the mechanical properties of alloy can be improved with the increase of injection speed and additional pressure. While the additional pressure is 35 MPa and the injection speed is 4.5 m/s, the tensile strength and elongation rate can reach 237.5 MPa and 4.8%, respectively. Through the microstructure analysis, the semi-solid thixo-casting most obviously refines the crystal grain. The solid phase particles in the semi-solid ingot may be broken into pieces again and the liquid phase may be sprayed and solidified during filling process due to most high shearing strength.

 

Key words: magnesium alloy; thixo-forming; semi-solid die casting; isothermal heat treatment; mechanical properties

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com